根據德國標準DIN50150,以下是常用范圍的鋼材抗拉強度與維氏硬度、布氏硬度、洛氏硬度的對照表。
Rm N/mm2 | 維氏硬度HV | 布氏硬度HB | 洛氏硬度HRC | 洛氏硬度HRB |
250 | 80 | 76.0 | - | |
270 | 85 | 80.7 | - | |
285 | 90 | 85.2 | - | |
305 | 95 | 90.2 | - | |
320 | 100 | 95.0 | - | |
335 | 105 | 99.8 | - | |
350 | 110 | 105 | - | |
370 | 115 | 109 | - | |
380 | 120 | 114 | - | |
400 | 125 | 119 | - | 64.5 |
415 | 130 | 124 | - | 67.5 |
430 | 135 | 128 | - | 70 |
450 | 140 | 133 | - | 73 |
465 | 145 | 138 | - | 75 |
480 | 150 | 143 | - | 77 |
490 | 155 | 147 | - | 78 |
510 | 160 | 152 | - | 80 |
530 | 165 | 156 | - | 82.1 |
545 | 170 | 162 | - | 84 |
560 | 175 | 166 | - | 84.9 |
575 | 180 | 171 | - | 86 |
595 | 185 | 176 | - | 87.5 |
610 | 190 | 181 | - | 88.6 |
625 | 195 | 185 | - | 89.6 |
640 | 200 | 190 | - | 90.9 |
660 | 205 | 195 | - | 92 |
675 | 210 | 199 | - | 93 |
690 | 215 | 204 | - | 94 |
705 | 220 | 209 | - | 95 |
720 | 225 | 214 | - | 95.6 |
740 | 230 | 219 | - | 97 |
755 | 235 | 223 | - | 97.5 |
770 | 240 | 228 | 20.3 | 98.4 |
785 | 245 | 233 | 21.3 | 99 |
800 | 250 | 238 | 22.2 | 100 |
820 | 255 | 242 | 23.1 | 101 |
835 | 260 | 247 | 24.0 | |
850 | 265 | 252 | 24.8 | |
865 | 270 | 257 | 25.6 | |
880 | 275 | 261 | 26.4 | 103 |
900 | 280 | 266 | 27.1 | |
915 | 285 | 271 | 27.8 | |
930 | 290 | 276 | 28.5 | |
950 | 295 | 280 | 29.2 | 105.5 |
965 | 300 | 285 | 29.8 | |
995 | 310 | 295 | 31.0 | |
1030 | 320 | 304 | 32.2 | |
1060 | 330 | 314 | 33.3 | |
1095 | 340 | 323 | 34.4 | |
1125 | 350 | 333 | 35.5 | |
1115 | 360 | 342 | 36.6 | |
1190 | 370 | 352 | 37.7 | |
1220 | 380 | 361 | 38.8 | |
1255 | 390 | 371 | 39.8 | |
1290 | 400 | 380 | 40.8 | |
1320 | 410 | 390 | 41.8 | |
1350 | 420 | 399 | 42.7 | |
1385 | 430 | 409 | 43.6 | |
1420 | 440 | 418 | 44.5 | |
1455 | 450 | 428 | 45.3 | |
1485 | 460 | 437 | 46.1 | |
1520 | 470 | 447 | 46.9 | |
1555 | 480 | (456) | 47.7 | |
1595 | 490 | (466) | 48.4 | |
1630 | 500 | (475) | 49.1 | |
1665 | 510 | (485) | 49.8 | |
1700 | 520 | (494) | 50.5 | |
1740 | 530 | (504) | 51.1 | |
1775 | 540 | (513) | 51.7 | |
1810 | 550 | (523) | 52.3 | |
1845 | 560 | (532) | 53.0 | |
1880 | 570 | (542) | 53.6 | |
1920 | 580 | (551) | 54.1 | |
1955 | 590 | (561) | 54.7 | |
1995 | 600 | (570) | 55.2 | |
2030 | 610 | (580) | 55.7 | |
2070 | 620 | (589) | 56.3 | |
2105 | 630 | (599) | 56.8 | |
2145 | 640 | (608) | 57.3 | |
2180 | 650 | (618) | 57.8 | |
660 | 58.3 | |||
670 | 58.8 | |||
680 | 59.2 | |||
690 | 59.7 | |||
700 | 60.1 | |||
720 | 61.0 | |||
740 | 61.8 | |||
760 | 62.5 | |||
780 | 63.3 | |||
800 | 64.0 | |||
820 | 64.7 | |||
840 | 65.3 | |||
860 | 65.9 | |||
880 | 66.4 | |||
900 | 67.0 | |||
920 | 67.5 | |||
940 | 68.0 |
硬度試驗是機械性能試驗中最簡單易行的一種試驗方法。為了能用硬度試驗代替某些機械性能試驗，生產上需要一個比較準確的硬度和強度的換算關系。
實踐證明，金屬材料的各種硬度值之間，硬度值與強度值之間具有近似的相應關系。因為硬度值是由起始塑性變形抗力和繼續塑性變形抗力決定的，材料的強度越高，塑性變形抗力越高，硬度值也就越高。
|